Abstract
Calcium-ion batteries (CBs) represent a sustainable and high-energy-density alternative to state-of the-art lithium-ion technology, yet their advancement is limited by the lack of high-performance intercalation cathodes. Identified via computational screening, post-spinel CaV2O4 has emerged as a promising candidate, though its practical application is hindered by limited electrochemical capacity. To rationalize the limitations associated with CaV2O4, we investigate the thermodynamic and ionic transport characteristics of CaxV2O4 (0 ≤ x ≤ 1) in this work. By integrating the cluster expansion formalism with Monte Carlo simulations and density functional theory based calculations, we construct the temperature-composition phase diagram of CaxV2O4, which reveals a complex phase behavior with Ca (de)intercalation consisting of several single phases (α through ζ) that can appear under electrochemical operating conditions at different voltages versus Ca/Ca2+. Importantly, we observe the formation of the ε phase at x ∼ 0.83 across a temperature window of 370-590 K via invariant reactions, which agrees with observations of subtle slope changes in the experimental voltage profiles. Further, migration barrier calculations confirm that Ca mobility is severely impeded within the α (x ∼ 0) and γ (x ∼ 0.5) phases, with the strong Ca-vacancy ordering contributing to the high barrier in the γ phase. Given the persistent two-phase region stretching across the δ (x ∼ 0.67) and the γ phases, and the poor Ca mobility in the γ phase, we expect the accessible electrochemical capacity in the CaV2O4 system to be kinetically limited to at most half the theoretical capacity at 298 K, in agreement with experimental observations. Strategies including cation doping and particle size reduction can be considered to flatten the potential energy landscape of the γ phase and improve Ca mobility as a result. Our computational findings establish a theoretical rationale for the experimentally observed low capacity in CaV2O4, highlight the interplay between thermodynamic stability and ionic transport, and provide design strategies that can enable the practical use of CaV2O4 as a CB cathode.